Two-dimensional graphitic carbon-nitride (g-C3N4)-coated LiNi0.8Co0.1Mn0.1O2 cathodes for high-energy-density and long-life lithium batteries
  • +1
  • Zhenliang Duan,
  • Pengbo Zhai,
  • Ning Zhao,
  • Xiangxin Guo
Zhenliang Duan
Qingdao University College of Materials Science and Engineering
Author Profile
Pengbo Zhai
Qingdao University College of Physics
Author Profile
Ning Zhao
Qingdao University College of Physics
Author Profile
Xiangxin Guo
Qingdao University College of Physics

Corresponding Author:[email protected]

Author Profile

Abstract

High-capacity nickel-rich layered oxides are promising cathode materials for high-energy-density lithium batteries. However, the poor structural stability and severe side reactions at the electrode/electrolyte interface result in unsatisfactory cycle performance. Herein, the thin layer of two-dimensional (2D) graphitic carbon-nitride (g-C3N4) is uniformly coated on the LiNi0.8Co0.1Mn0.1O2 (denoted as NCM811@CN) using a facile chemical vaporization-assisted synthesis method. As an ideal protective layer, the g-C3N4 layer effectively avoids direct contact between the NCM811 cathode and the electrolyte, preventing harmful side reactions and inhibiting secondary crystal cracking. Moreover, the unique nano-pore structure and abundant nitrogen vacancy edges in g-C3N4 facilitate the adsorption and diffusion of lithium ions, which enhances the lithium deintercalation/intercalation kinetics of the NCM811 cathode. As a result, the NCM811@CN-3wt% cathode exhibits 161.3 mAh g-1 and capacity retention of 84.6% at 0.5 C and 55 °C after 400 cycles and 95.7 mAh g-1 at 10 C, which is greatly superior to the uncoated NCM811 (i.e. 129.3 mAh g-1 and capacity retention of 67.4% at 0.5 C and 55 °C after 220 cycles and 28.8 mAh g-1 at 10 C). The improved cycle performance of the NCM811@CN-3wt% cathode is also applicable to solid-liquid-hybrid cells composed of PVDF:LLZTO electrolyte membranes, which show 163.8 mAh g-1 and the capacity retention of 88.1% at 0.1 C and 30 °C after 200 cycles and 95.3 mAh g-1 at 1 C.
03 Mar 2024Submitted to Energy & Environmental Materials
12 Mar 2024Submission Checks Completed
12 Mar 2024Assigned to Editor
13 Mar 2024Review(s) Completed, Editorial Evaluation Pending
16 Mar 2024Reviewer(s) Assigned
08 Apr 2024Submission Checks Completed
08 Apr 2024Assigned to Editor
15 Apr 2024Review(s) Completed, Editorial Evaluation Pending
23 Apr 2024Editorial Decision: Accept